Key Features
- Advanced Silver/Carbon filled epoxy
- Excellent electrical conductivity, volume resistivity ≤ 0.0007 Ω·cm
- Enhanced bonding to various substrates: glass, metals, plastics.
- Perfect for die attachment and solderless interconnections.
- Affordable alternative to pure silver epoxies
Intro
Conductive epoxies can be used to form an electrically conductive bond between dissimilar materials eliminating need for soldering. Traditional silver-based epoxy materials require up to 80% weight load of silver fillers and as a result tend to be costly, brittle and prone to mechanical failure.
Our Conductive Silver/Carbon Epoxy G6E-NS11 has been developed based on advanced proprietary technology that requires 20% or less silver content to be at par with leading silver based epoxies in terms of electrical properties. This improvement not only brings price of the material down but also makes G6E-NS11™ less prone to fracture and allow for stronger adhesion to the target substrate.
Silver/Carbon Epoxy G6E-NS11™ is a two component adhesive for high performance bonding, sealing and coating purposes. G6E-NS11™ is intended to be cured at elevated temperatures. It can cure at room temperature in 60 hours or much more rapidly at elevated temperatures. Recommended curing temperature is 150°C. Volume resistivity of as low as 0.0007 Ω·cm can be achieved under optimum curing conditions.
G6E-NS11™ has smooth paste like consistency after mixing and bonds well to a wide variety of substrates including metals, composites, ceramics, glass and plastics. It has limited adhesion to rubber and silicon-based materials. This product is recommended for electronic packaging applications such as die attachment and solderless interconnections, component repair, display interconnections.
TWO COMPONENT SYSTEM: Part A – smooth thixotropic dark grey paste, Part B – smooth thixotropic silver paste.
THE MIX RATIO: 100 (Part A) to 100 (Part B) by weight.
CURING INSTRUCTIONS: Best results are obtained when product is cured at one of the following parameters: 60 hours @ 25°C, 3 hours @ 70°C or 1 hour @ 150°C
COLOR: Part A: grey, Part B: silver grey
POT LIFE: 4 hours
GLASS TRANSITION TEMPERATURE: 65°C (cured at 150°C)
MIXED VISCOSITY AT 25°C/77°F: 80-85 Pa.s
HARDNESS, SHORE: >65D
VOLUME RESISTIVITY: ≤ 0.0007 Ω·cm
STORAGE: Shelf life: 6 months at 25°C in unopened, unmixed containers. Stores and ships at room temperature—no freezing or dry ice required.
MIXING INSTRUCTIONS: Stir both components before use. Add Part B to Part A and mix slowly until uniform in a separate container.
SAFETY & HANDLING: Please read the SDS before use. Provide adequate ventilation and keep away from sparks and open flames. Avoid prolonged exposure to skin and breathing of vapors. Wash with plenty of soap and water to remove any residue from the skin.
PACKAGING: Silver/Carbon Epoxy G6E-NS11™ has components Part A and Part B packaged in 10g, 20g and 50g each for 3 different quantities currently in offer. However, this product can be customized in any desired quantity based upon the customer's need.
Application Notes
- Attachment of electro optical components
- Grounding
Repair of defect traces / tracks or creating smooth jumpers on PCB board.
- Lightning Strike Protection and EMI/RFI Shielding
- Lower temperature bonding of electrical modules
- High frequency shields, waveguides
- Terminal attachment to solar cell panels
- Quick and inexpensive mounting of LEDs
- Conductive traces on 3D printed parts
- Radio-frequency identification (RFID) tags
- 3D antennas
Easy repair of household electronics and car rear shield heater.
|
|
|
 |
|
 |
|